    ASTM D4786–00 缝合抗撕裂强度单孔试验方法


    Designation: ASTM D4786–00 缝合抗撕裂强度单孔试验方法

    Standard Test Method for

    Stitch Tear Strength, Single Hole1

    This standard is issued under the fixed designation D 4786; the number immediately following the designation indicates the year of

    original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A

    superscript epsilon (e) indicates an editorial change since the last revision or reapproval.

    1. Scope

    1.1 This test method is intended for determining the stitchtearing

    strength of leather with a tear originating from one

    hole. It is particularly applicable to heavy leather. This test

    method does not apply to wet blue.

    1.2 This standard does not purport to address all of the

    safety concerns, if any, associated with its use. It is the

    responsibility of the user of this standard to establish appropriate

    safety and health practices and determine the applicability

    of regulatory limitations prior to use.

    2. Referenced Documents

    2.1 ASTM Standards:

    D 1813 Test Method for Measuring Thickness of Leather

    Test Specimen2

    D 2209 Test Method for Tensile Strength of Leather2

    3. Significance and Use

    3.1 This test method is intended to be used to rate leathers

    as to their stitch tear strengths.

    4. Apparatus

    4.1 Thickness Gage—A dead-mass type of thickness gage,

    as described in Test Method D 1813.

    4.2 Steel Punch, beveled on the outside, which will make a

    18in. diameter hole.

    4.3 Metal Yoke, made to the dimension shown in Fig. 1.

    4.4 Steel Rod, 0.0950.005 in. in diameter and at least 1 in.

    long.

    4.5 Testing Machine, power-driven, as described in Test

    Method D 2209.

    5. Test Specimen

    5.1 The test specimen shall be a rectangular piece of leather

    1 in. by 2 in. die cut from the sample unit of leather. The end

    of the specimen in which the hole is to be punched shall be at

    least 1 in. away from any uncut edge on the unit. The direction

    of the long axis relative to the backbone shall be noted.

    6. Procedure

    6.1 Place the specimen on the anvil of the thickness gage

    and lower the presser foot gently (do not drop) until it rests on

    the specimen. Take the reading 5 s after the full load is reached.

    Read the thickness to the nearest 0.001 in. The thickness of the

    specimen should be taken on the long axis near the end in

    which the hole is to be punched.

    6.2 Punch a 18in. diameter hole on the long axis of the

    specimen. The center of the hole should be 532 in. from the end

    on which the thickness was measured.

    6.3 Grip the yoke in one of the testing machine jaws. Place

    the end of the specimen containing the hole between the arms

    of the yoke and pass the steel rod through the holes in the yoke

    and the specimen. Clamp the free end of the specimen in the

    other testing machine grip. Operate the machine at 10 2 in.

    per minute until the specimen starts to tear. At the instant that

    tearing begins, note and record the load registered by the

    machine.

    7. Calculation

    7.1 Calculate the pounds per in. thickness as follows:

    T = thickness of sample Avg stitch tear strength 5

    F/T

    S

    S = Number of individual specimens per unit test of leathers

    8. Report

    8.1 Report should include the following:

    8.1.1 Stitch tear strength of each test specimen and average

    stitch tear strength per unit of leather.

    8.1.2 The thickness measurements of all the specimens

    tested shall be averaged to the nearest 0.001 in. and reported as

    the thickness of the sample unit of leather.

    8.1.3 The direction of the long axis of the specimen relative

    to the back-bone shall be reported.

    9. Precision and Bias

    9.1 This test method is adopted from the procedures of the

    American Leather Chemist Association where it has long been

    in use and where it was approved for publication before the

    inclusion of precision and bias statements was mandated. The

    original interlaboratory test data is no longer available. The

    user is cautioned to verify by the use of reference materials, if

    available, that the precision and bias of this test method is

    adequate for the contemplated use.

    10. Keywords

    10.1 leather; stitch tear strength; tear strength

    The American Society for Testing and Materials takes no position respecting the validity of any patent rights asserted in connection

    with any item mentioned in this standard. Users of this standard are expressly advised that determination of the validity of any such

    patent rights, and the risk of infringement of such rights, are entirely their own responsibility.

    This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and

    if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards

    and should be addressed to ASTM Headquarters. Your comments will receive careful consideration at a meeting of the responsible

    technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your

    views known to the ASTM Committee on Standards, at the address shown below.

    This standard is copyrighted by ASTM, 100 Barr Harbor Drive, PO Box C700,West Conshohocken, PA 19428-2959, United States.

    Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above address or at